Quaternary vitreous solid lithium cation conductive electrolyte

ABSTRACT

A solid state electrolyte for a solid state cell system comprising a quaternary vitreous lithium cation conductor having a conductivity of at least 0.75x10-4ohm-1cm-1 at 25 DEG  C.

DESCRIPTION OF THE INVENTION

1. Technical Field

The invention relates to a quaternary solid state electrolyte based on a vitreous lithium cation conductor of the composition:

    aX, bLi.sub.2 S, Y, Z

where:

X is selected from the group consisting of P₂ S₅ and SiS₂ ;

a is from about 0.5 to about 2;

b is from 0.25 to 2;

Y is an oxygen-containing lithium compound selected from the group consisting of Li₂ CO₃, Li₂ SiO₃ and Li₄ SiO₄ ;

Z is a dopant selected from the group consisting of LiI, LiBr, LiCl and LiF; and wherein said composition has a conductivity of at least 0.75×10⁻⁴ ohm⁻¹ cm⁻¹ at 25° C.

2. Background of the Art

Ionic conductivity is usually associated with the flow of ions through a liquid solution of salts. In the vast majority of practical uses of ionic conductors, i.e, as electrolytes for dry cell batteries, the liquid solution is immobilized in the form of a paste or gelled matrix or is absorbed in a separator to overcome the difficulties associated with handling and packaging a liquid. However, even after immobilization, the system is still subject to possible leakage, has a limited shelf life due to drying out or crystallization of the salts and is suitable for use only within a limited temperature range corresponding to the liquid range of the electrolyte. In addition, the use of a large volume of immobilizing material has hindered the aims of miniaturization.

In addition, improved microelectronic circuit designs have generally decreased the current requirements for electronic devices. This in turn has enhanced the applicability of solid electrolyte power sources which usually can deliver currents only in the microampere range. These solid electrolyte systems have the inherent advantages of being free of electrolyte leakage and internal gassing problems due to the absence of a liquid phase. In addition, they also have a much longer shelf life than the conventional liquid electrolyte power sources.

In attempting to avoid the shortcomings of liquid systems, investigators have surveyed a large number of solid compounds seeking to find compounds which are solid at room temperature and have specific conductances approaching those exhibited by the commonly used liquid systems. Solid electrolytes must be essentially electronic insulators so as not to internally short the cell while at the same time they must allow ionic migration in the crystal lattice for the cell to operate. It has been discovered that certain metallic salts which are solids at room temperature have specific conductances sufficiently high to permit their use in practical battery applications. For example, U.S. Pat. No. 3,723,185 discloses solid state electrolytes of compounds conforming to the general formula AgI--MCN--AgCN or modifications thereof where M is potassium, rubidium, cesium or mixtures thereof.

U.S. Pat. No. 4,331,750 discloses a cation conductive vitreous composition suitable for use as a solid electrolyte and having the general formula:

    aP.sub.2 S.sub.5, bLi.sub.2 S, cLiX

where:

X represents chlorine, bromine or iodine: c is greater than or equal to 0; the ratio b/(a+b) lies between 0.61

and 0.70; and

the ratio c/(a+b+c) is less than or equal to a limit which corresponds to solubility in the vitreous phase of LiX in the composition aP₂ S₅, bLi₂ S.

U.S. Pat. No. 4,465,746 discloses a solid state electrolyte based on vitreous lithium cation conductor of the composition:

    SiS.sub.2, xLi.sub.2 S, yLiI

where:

x is from 0.8 to 1.5,

y is from 0 to about 2, and wherein said composition has a conductivity of at least 0.75×10⁻⁴ ohm⁻¹ cm⁻¹ at 25° C.

U.S. Pat. No. 4,513,070 discloses an electrochemical device which uses a vitreous material having a general formula

    xA.sub.a R.sub.b --yN.sub.m R.sub.c --zN.sub.n Y.sub.p

wherein a is Si, Ge, P, S, B, Nb, As, V, Cr or Mo; R is O, S or Se; N is Li, Na, K or Ag and Y is I, Br, Cl, F, ClO₄, CF₃ SO₃, SCN or SO₄ with the proviso that the material contain at least two salts N_(n) Y_(p) and wherein a, b; m, c and n, p represent the indices corresponding to the stoichiometry of the constituents in a given group and x, y and z, whose sum is equal to 1, represent the indices corresponding to the overall molar fractions respectively of the compound or compounds forming the former system, the modifier system and the doping salt of the material, the values of these indices being compatible with the vitreous range of a given material.

It is an object of the present invention to provide a new class of quaternary vitreous compositions that can be used as solid electrolytes in solid state cell systems.

Another object of the invention is to provide a SiS₂ -based or P₂ S₅ -based vitreous lithium cation conductor which contains a lithium oxide compound and which has a conductivity of at least 0.75×10⁻⁴ ohm⁻¹ cm⁻¹ at 25° C.

The foregoing and additional objects will become more fully apparent from the following description.

DISCLOSURE OF THE INVENTION

The invention relates to a quaternary solid electrolyte having a vitreous lithium cation conductor of the composition:

    aX, bLi.sub.2 S, Y, Z

where

X is selected from the group consisting of P₂ S₅ and SiS₂ ;

a is from about 0.5 to about 2;

b is from 0.25 to 2;

Y is an oxygen-containing lithium compound selected from the group consisting of Li₂ CO₃, Li₂ SiO₃ and Li₄ SiO₄ ;

Z is a dopant selected from the group consisting of LiI, LiBr, LiCl and LiF; and wherein said composition has a conductivity of at least 0.75×10⁻⁴ ohm⁻¹ cm⁻¹ at 25° C.

In the above quaternary composition b is preferably between about 1 and about 2. As used herein, vitreous shall mean a composition in a glassy (non-crystalline) state and shall also include materials that have been cooled so rapidly from the molten condition that crystal formation is prevented.

When X is SiS₂, then the vitreous composition of SiS₂ and Li₂ S or Li₂ SiS₃ can be prepared at 1 atmosphere pressure by first mixing silicon disulfide (SiS₂) and lithium sulfide (Li₂ S) in 1:1 mole ratio in an inert gas filled dry box. The mixture is then placed in a vitreous carbon crucible which in turn is placed in an inert gas reaction chamber. The SiS₂ and Li₂ S mixture is heated at an elevated temperature for a time period sufficient for the SiS₂ to react with the Li₂ S to form Li₂ SiS₃. Generally, the SiS₂ and Li₂ S mixture can be heated at about 950° C. for about 6 hours. The Li₂ SiS₃ is then quenched to ambient temperature (about 20° C.) to form the vitreous solid. If desired, the lithium compound can be added by grinding together the vitreous Li₂ SiS₃ and the lithium compound, placing the mixture in a vitreous carbon crucible and then heating the mixture at an elevated temperature for a time period sufficient to form a solution of the lithium compound in the Li₂ SiS₃ material. The material is then quenched to room temperature. Generally the mixture can be heated at about 950° C. for about 6 hours and then quenched to room temperature.

Using the above technique, Li₂ S and SiS₂ can be fused with Li₂ CO₃, Li₂ SiO₃ or Li₄ SiO₄ and a dopant such as LiI, LiBr, LiCl or LiF to produce vitreous compositions all having conductivity in excess of 10⁻⁴ ohm⁻¹ cm⁻¹. The addition of Li₂ CO₃ and a dopant to Li₂ SiS₃ and then fusing the materials resulted in a red-brown glass with excellent conductivity. Additionally, Li₂ CO₃ assists in formation of a vitreous product since fusion of Li₂ S+SiS₂ at 950° C. followed by a cold water quench to 20° C. often results in a crystalline and/or opaque material, whereas fusion and quenching of material containing Li₂ CO₃ results in a clear reddish-brown glass. Indeed, even slow cooling the fused materials containing Li₂ CO₃ results in a clear reddish-brown glass. Thus lithium carbonate significantly and unexpectedly aids in forming and maintaining the vitreous state such that the need to rapidly quench the melt is lessened. Lithium metasilicate, Li₂ SiO₃, also forms a highly cationically conductive glass with Li₂ SiS₃.

P₂ S₅ -based vitreous compositions can be prepared by melting together the components P₂ S₅, Li₂ S, a dopant and the lithium compound at a temperature which lies between 700° C. and 950° C., followed by tempering and then by annealing at a temperature of about 100° C. If desired, the P₂ S₅ and Li₂ S components can be first heated and then the lithium compound and dopant can be added. However, the synthesis of P₂ S₅ -based materials must be performed in sealed vessels due to the volatility of P₂ S₅.

The lithium compounds for use in the invention are Li₂ CO₃, Li₂ SiO₃, and Li₄ SiO₄. These lithium compounds Li₂ CO₃, Li₂ SiO₃ and Li₄ SiO₄ are believed to be network formers and not dopants while LiI, LiF, LiBr and LiCl are the dopants. Network former is a compound which provides a macromolecular network of irregular structure whereby the anion of the network former, i.e., O⁼, S⁼, etc., forms bridges between the cations of the network former resulting in the formation of an extended network. Network modifier is an ionic compound added to a network former which introduces covalency into the macromolecular network by incorporating its anion into the macromolecular network by cleavage of some of the bridges between the network former cation and the associated network former anion and bonding the modifier anion to the network former cation. Network dopant is a compound added to a network former or the network former plus network modifier which provides additional mobile cations but whose associated anion does not become incorporated into the macromolecular structure but rather plays a role more like a plasticizer especially in the case of halogenated salts.

Anode materials suitable for use with the solid electrolyte of this invention include lithium, silver, sodium, potassium, and rubidium. The preferred anode materials are lithium and lithium alloys.

Cathodes suitable for use with the solid electrolyte of this invention include poly(N-vinylpyrrolidone) (PVP)+iodine, PVP+iodine+TiS₂, FeS₂, Sb₂ S₃, TiS₂, MoS₃, TiS₂ +MoS₃, organic charge transfer complexes with halogens, and MnO₂.

EXAMPLE 1

Vitreous Li₂ SiS₃ was prepared by mixing 30 grams SiS₂ and 15 grams Li₂ S in 1:1 mole ratio in a helium-filled dry box. The mixture was placed in a vitreous carbon crucible which in turn was placed in a vitreous silica reaction tube. The tube was closed and was equipped with a conventional exhaust vent and a small conventional intake feed tube adapted for feeding helium into the reaction tube. The SiS₂ and Li₂ S mixture, under a 1 atmosphere pressure of helium, was heated at 950° C. for 6 hours and then the reaction tube was quenched to room temperature (20° C.) by submerging the reaction tube in cold water. The vitreous Li₂ SiS₃ solid electrolyte produced was then ground.

The vitreous Li₂ SiS₃ produced was combined with Li₂ CO₃ and LiBr or LiI. The mixture was ground, placed in a vitreous carbon crucible and then placed in a reaction tube. Under 1 atmosphere helium pressure, the Li₂ SiS₃, Li₂ CO₃ and LiI or LiBr mixtures were each heated at 950° C. for 6 hours and then the reaction tube was quenched to room temperature (20° C.) by submerging the reaction tube in cold water. The quaternary vitreous solid electrolytes produced were ground, pelletized and found to have a conductivity as shown in Table 1.

Specifically the conductivity was measured by pelletizing (via the application of uniaxial pressure) the powdered material between titanium disulfide electrodes at 13,000 psi in a conventional steel mold with steel rams. The disc of solid electrolyte with TiS₂ electrodes was ejected from the mold and then heat sealed in a polyethylene bag. The sample sealed in the bag was then placed in an alcohol-filled polytetrafluoroethylene cylinder with a tight fitting lid which was in turn placed in a large steel mold fitted with steel rams. The alcohol-filled polytetrafluoroethylene cylinder containing the sample was then compressed to 54,000 psi which results in an isostatic compression of the glass sample disc and its associated electrodes. The TiS₂ /solid electrolyte/TiS₂ sample was placed in a spring-loaded holder fitted with gold contacts. The conductivity of the sample was measured using the complex plane technique first applied to solid electrolytes by J. E. Bauerle, J. Phys. Chem. Solids, 30,657 (1969). The complex plane technique is at present almost universally applied for the measurement of conductivity of solid electrolytes.

                  TABLE 1                                                          ______________________________________                                         Conductivity at 25° C.                                                  Vitreous            Conductivity                                               Composition         ohm.sup.-1 cm.sup.-1                                       ______________________________________                                         Li.sub.2 SiS.sub.3.0.25LiBr.0.1875Li.sub.2 CO.sub.3                                                4.7 × 10.sup.-4                                      Li.sub.2 SiS.sub.3.0.5LiBr.0.37Li.sub.2 CO.sub.3                                                   1.04 × 10.sup.-4                                     Li.sub.2 SiS.sub.3.0.25LiI.0.375Li.sub.2 CO.sub.3                                                  2.3 × 10.sup.-4                                      ______________________________________                                    

EXAMPLE 2

A 0.787 inch diameter by 0.063 inch high coin cell was constructed as follows. A cathode composed of TiS₂ containing some solid electrolyte of 0.25LiI.0.375Li₂ CO₃.Li₂ SiS₃ and powdered aluminum as a conductivity aid was employed. The TiS₂ cathode along with a separate layer of 0.25LiI.0.375Li₂ CO₃.Li₂ SiS₃ electrolyte as prepared in Example 1 and a lithium anode were isostatically compressed at 80,000 psi as described in U.S. Pat. No. 4,477,545 and then assembled into the cell housing. The cell was continuously discharged at ambient temperature across a 30 Kohm load to a 1.4 volt cutoff. The voltage readings observed with time are shown in Table 2.

                  TABLE 2                                                          ______________________________________                                         Li/0.25LiI.0.375Li.sub.2 CO.sub.3.Li.sub.2 SiS.sub.3 /TiS.sub.2                Voltage (volts)                                                                               Time (hours)                                                    ______________________________________                                         2.42            0                                                              2.17           16                                                              1.99           40                                                              1.74           64                                                              1.41           88                                                              ______________________________________                                    

It should be understood that the foregoing disclosure relates to preferred embodiments of the invention and it is intended to cover all changes and modifications of the invention which do not depart from the spirit and scope of the appended claims. 

What is claimed:
 1. A quaternary solid state electrolyte having a vitreous lithium cation conductor of the composition:

    aX, bLi.sub.2 S, Y, Z

where X is selected from the group consisting of P₂ S₅ and SiS₂ ; a is from about 0.5 to about 2; b is from 0.25 to 2; Y is an oxygen-containing lithium compound selected from the group consisting of Li₄ SiO₄, Li₂ CO₃ and Li₂ SiO₃ ; Z is a dopant selected from the group consisting of LiI, LiBr, LiCl and LiF; and wherein said composition has a conductivity of at least 0.75×10⁻⁴ ohm⁻¹ cm⁻¹ at 25° C.
 2. The solid state electrolyte of claim 1 wherein X is SiS₂.
 3. The solid state electrolyte of claim 1 wherein X is P₂ S₅.
 4. The solid state electrolyte of claim 1 or 2 wherein the quaternary vitreous lithium cation conductor is Li₂ SiS₃.0.25LiBr.0.1875Li₂ CO₃.
 5. The solid state electrolyte of claim 1 or 2 wherein the quaternary vitreous lithium cation conductor is Li₂ SiS₃.0.5LiBr.0.375 Li₂ CO₃.
 6. The solid state electrolyte of claim 1 or 2 wherein the quaternary vitreous lithium cation conductor is Li₂ SiS₃.0.25LiI.0.375 Li₂ CO₃.
 7. A solid state cell comprising an anode, a cathode and a quaternary vitreous lithium cation conductor of the composition:

    aX, bLi.sub.2 S, Y, Z

where X is selected from the group consisting of P₂ S₅ and SiS₂ ; a is from about 0.5 to about 2; b is from 0.25 to 2; Y is an oxygen-containing lithium compound selected from the group consisting of Li₂ SiO₃, Li₂ CO₃ and Li₄ SiO₄ ; Z is a dopant selected from the group consisting of LiI, LiBr, LiCl and LiF; and wherein said composition has a conductivity of at least 0.75×10⁻⁴ ohm⁻¹ cm⁻¹ at 25° C.
 8. The solid state cell of claim 7 wherein X is P₂ S₅.
 9. The solid state cell of claim 7 wherein X is SiS₂.
 10. The solid state cell of claim 7 wherein the vitreous lithium cation conductor is Li₂ SiS₃.0.25LiBr.0.1875Li₂ CO₃.
 11. The solid state cell of claim 7 wherein the vitreous lithium cation conductor is Li₂ SiS₃.0.5LiBr.0.375Li₂ CO₃.
 12. The solid state cell of claim 7 wherein the vitreous lithium cation conductor is Li₂ SiS₃.0.25LiI.0.375Li₂ CO₃.
 13. The solid state cell of claim 7 wherein the anode is selected from the group consisting of lithium, lithium alloys, sodium, potassium, rubidium, and silver.
 14. The solid state cell of claim 7 wherein the cathode is selected from the group consisting of TiS₂, MoS₃, PVP+I₂, PVP+I+TiS₂, TiS₂ +MoS₃, FeS₂, Sb₂ S₃, and MnO₂.
 15. The solid state cell of claim 7 wherein the anode is lithium, and the cathode is TiS₂.
 16. The solid state cell of claim 7 wherein the anode is lithium and the cathode is TiS₂ +MoS₃. 